SME 6013

DETAILS

Features/Characteristics

SME6013 is very similar to the E6012 electrodes, have distinct differences. E6013 electrodes were designed specifically for light sheet metal work. However, the larger diameters are used on many of the same applications as E6012 electrodes and provide low penetrating arc. Coverings of E6013 electrodes contain rutile, cellulose, ferromanganese, potassium silicate as a binder, and other siliceous materials. The potassium compounds permit the electrodes to operate with ac at low amperages And low open-circuit voltages. E6013 electrodes are similar to the E6012 electrodes in usability characteristics and bead appearance. The arc action tends to be quieter and the bead surface smoother with a finer ripple.

SME 6013 Welding Rod Uses/Applications

1. SME6013 electrodes recommended for sheet metal applications where their ability to weld satisfactorily in the vertical welding position with downward progression
2. Usually produce the best radiographic soundness in welding small, thin parts, used also Joining Steels like A, B, C, D grade of ASTM -283
3. Used for storage tanks, wagons, automobile frames and bodies, rolling stocks, rail coaches locomotive fire boxes, etc.
4. General purpose fabrication, Thin sheet metal welding, Excessively machined and damaged mild steel

Welding Positions

F, H, V-down, V-up, OH

Re-drying Conditions

For best result achievement Re-Dry Electrodes at 100 °C for½ hour to 1 Hour.

Disclaimers

Service Information

Documentation

• Safety Data Sheet
• Certificates of Conformance

More Mild Steel Electrodes

CONFORMANCE/ CLASSIFICATION

SME 6013 WELD COMPOSITION

MECHANICAL PROPERTIES

Ultimate Tensile Strength Min: 430 MPa

Yield Strength Min: 330 MPa

Elongation Min: 17 %

TYPICAL OPERATING PROCEDURES (WELDING CURRENT) AC, DC(-)

Availability

Standard Size: 5.0, 4.0, 3.15, and 2.5 diameter.